| FDM成形工艺对轻量化液压阀块力学性能的影响 |
| Effect of FDM Forming Process on Mechanical Properties of Lightweight Hydraulic Valve Block |
| |
| DOI：10.16018/j.cnki.cn32-1650/n.202301009 |
| 中文关键词: FDM 液压阀块 正交试验 力学性能 |
| 英文关键词: FDM hydraulic valve block orthogonal test mechanical property |
| 基金项目: |
|
| 摘要点击次数: 822 |
| 全文下载次数: 908 |
| 中文摘要: |
| 结合增材制造轻量化、节能化液压阀块的设计准则，设计了一种轻量化液压阀块，利用熔融沉积成形技术(FDM)制造成形。通过正交试验研究FDM成形工艺中的打印温度、层厚和填充率等因素对液压阀块力学性能的影响。结果表明，三因素对液压阀块试件最大承载力的影响由强到弱依次为层厚、打印温度、填充率，其中，层厚对试件最大承载力影响显著，三因素交互作用对试验结果没有影响；当打印温度为190 ℃，层厚为0. 3 mm，填充率为20%时，试件具有最大承载力；三因素对试件总吸能性的影响与其对试件最大承载力的影响结果一致，验证了该液压阀块力学性能正交试验结果的正确性。 |
| 英文摘要: |
| Based on the design criteria of lightweight and energy-saving hydraulic valve block in additive manufacturing, a lightweight hydraulic valve block was designed, and FDM was used to manufacture it. The effects of printing temperature, layer thickness, and filling ratio on the mechanical properties of hydraulic valve blocks in FDM forming process were studied through orthogonal experiments. The results show that the influence of the three factors on the maximum bearing capacity of the hydraulic valve block specimen from strong to weak is in order of layer thickness, printing temperature, and filling rate. Among them, the layer thickness has a significant impact on the maximum bearing capacity of the specimen, while the interaction of the three factors has no impact on the test results. When the printing temperature is 190 ℃, the layer thickness is 0. 3 mm, and the filling rate is 20%, the specimen has the maximum bearing capacity. The effects of three factors on the total energy absorption of the specimen are consistent with the results of their effects on the maximum bearing capacity of the specimen. The correctness of the orthogonal test results of the mechanical properties of the hydraulic valve block is verified. |
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |
|
|
|